Customized PVC Particles High Quality Compound Raw Material PVC Plastic Particles

• Customization: Available
• Carrier: PVC
• Color: Customized
• Model NO.: 385
• Certification: RoHS, ISO, CE
• Transport Package: 25kg/Bag
• Specification: 50kg per bag or customized
• Trademark: HebeiBaiyi
• Origin: China
• HS Code: 8545110000
• Production Capacity: 5000ton/Year

Product Description

Product Description

 

Product Description

Specifications PVC (Polyvinyl Chloride) is one of the most popular amorphous plastics. There are two kinds of PVC; one is hard type and the other is flexible or soft.
In the cable industry . Especially PVC having low temperature stability can easily stick to metallic surface when it's heated. PVC is widely used in cable industry because of its resistant for heavy weather condition, easy processing and better electrical properties.
If PVC is directly subjected to heat, HCl (hydrogen chloride) is disseminated and colour of the PVC gets yellow. Depending on the rate of corruption due to the heat, color of PVC changes to yellow, red, brown, black respectively. During the heating, all physical and chemical properties change. During the process, toxic gases disseminate and humidity are got away by vacuum. Some additional materials should also be used in production process. These are generally as followings;

PVC Formule
1. PVC Resin
2. Plastiphians
3. Stabilizetor
4. Lubricant
5. Filling (bedding) compound
6. Strength modifier
7. Compounds to facilitate of process
8. Pigments

Flame retardant and optic bledcher material can also be used with above. Different type PVC granules can be produced by changing the rate of the above materials in the granule according to the requirements of application field for final product.
PVC granules are mainly used as 2 different types in the cable industry as lifted below.

Technical specifications of 70 ºC pvc compound
 

Tensile Strength	MPa	20.5
Fracture Tensile Strain	%	320
Ageing Temperature	ºC	100
Ageing Time	h	168
Tensile Strength After Ageing	MPa	22.5
Max Change of Tensile Strength	%	+12
After Ageing Fracture Tensile Strain	%	290
Max Change of Fracture Tensile Strain	%	-10
Thermal Deformation	%	28
Thermal Ageing Quality Loss	g/m²	19
200ºC Thermal Stability Time	min	90
20ºC Volume Resistivity	Ω.cm	2.0*1011

Technical specifications of  90 ºC pvc compound
 

Tensile Strength	MPa	20
Fracture Tensile Strain	%	330
Ageing Temperature	ºC	100
Ageing Time	h	240
Tensile Strength After Ageing	MPa	21.5
Max Change of Tensile Strength	%	+8
After Ageing Fracture Tensile Strain	%	310
Max Change of Fracture Tensile Strain	%	-6
Thermal Deformation	%	28
Thermal Ageing Quality Loss	g/m²	9
200ºC Thermal Stability Time	min	120
20ºC Volume Resistivity	Ω.cm	2.0*1010

 

 

 

 

 

 

 

Detailed Photos

 

 

 

Packaging & Shipping

 

25kg/ carton or 25kg/bag, or per your requirement

25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container

Company Profile

 

FAQ

 

1. How can we guarantee quality?

Always a pre-production sample before mass production and final inspection before shipment.


2.what can you buy from us?

PP, ABS, HDPE, LDPE, LLDPE, PVC raw material.

3. why should you buy from us not from other suppliers?

We have excellent export team, third party inspection can be carried out before shipment.

4. What are your terms of payment?

T/T or LC.

5. Your packing?

Basically our packing is in 25/KG bags.