Physical Property Value Condition
|
|
|||
|
Density / Specific Gravity
|
1.20 g/cm³
|
23°C
|
ASTM D792
|
|
|
Melt Mass-Flow Rate, MFR
|
22 g/10min
|
300°C,1.2 kg
|
ASTMD1238
|
|
|
Rockwell Hardness, M-Scale
|
77
|
|
ASTM D785
|
|
|
Mechanical Property Value Condition Standard
|
|
|||
|
Tensile Strength, Yield
|
61.6 MPa
|
6 mm/min
|
ASTM D638
|
|
|
Tensile Elongation, Break
|
110%
|
6 mm/min
|
ASTM D638
|
|
|
Flexural Strength
|
89.8 MPa
|
1.3 mm/min
|
ASTM D790
|
|
|
Notched Izod Impact
|
820 J/m
|
23 °C 3.2 mm
|
ASTM D256
|
|
|
Thermal Property Value Condition Standard
|
||||
|
Deflection Temperature Under Load, Annealed
|
144 °C
|
0.45 MPa
132 °C x 8 hr |
ASTM D648
|
|
|
Flame
Rating |
V-2
|
0.38 mm
|
UL94
|
|
|
Flame
Rating |
V-2
|
3.2 mm
|
UL94
|
|
|
Processing Property Value Condition
|
||||
|
Drying Temperature
|
120 °C
|
|
|
|
|
Drying Time
|
4.0hr
|
|
|
|
|
High Amp Arc Ignition, HAI
|
PLC 0
|
|
UL 746
|
|
|
High Voltage Arc Tracking Rate,HVTR
|
80.0 - 150mm/min
|
|
UL 746
|
|
|
High Voltage Arc Tracking Rate,HVTR
|
PLC 3
|
|
UL 746
|
|
|
Hot-wire Ignition,HWI
|
30-60
sec |
|
UL 746
|
|
|
Hot-wire Ignition,HWI
|
PLC 2
|
|
UL 746
|
|
|
Thermal Property
|
Value Condition
|
|
||
|
HDT, Unannealed
|
135 °C
|
1.8 MPa
|
ASTM D648
|
|
|
RTI Elec
|
125 °C
|
|
UL 746
|
|
|
RTI Imp
|
115 °C
|
|
UL 746
|
|
|
RTI Str
|
125 °C
|
|
UL 746
|
|
|
FlameRating
|
V-0
|
3 mm
|
UL94
|
|
|
Processing Property Value Condition
|
|
|||
|
Drying Temperature
|
121 °C
|
|
|
|
|
Drying Time
|
3.0 - 4.0hr
|
|
|
|
25kg/ carton or 25kg/bag, or per your requirement