| General | ||
| Form Resin Pellets | ||
| Physical | Nominal Value | Test Method |
| Density / Specific Gravity | 1.13 g/cm³ | ASTM D792 |
| Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.70 % | Internal Method |
| Water Absorption(24 hr) | 0.10 % | ASTM D570 |
| Water Absorption, Equilibrium(23 °C) | 0.40 % | ASTM D570 |
| Mechanical | Nominal Value | Test Method |
| Tensile Modulus(50 mm/min) | 2060 MPa | ASTM D638 |
| Tensile Strength, Yield(50 mm/min;Type I) | 52.0 MPa | ASTM D638 |
| Tensile Elongation, Yield(50 mm/min;Type I) | 5.0 % | ASTM D638 |
| Tensile Elongation, Break(50 mm/min;Type I) | 100 % | ASTM D638 |
| Flexural Modulus(1.3 mm/min;50 mm;Span) | 2060 MPa | ASTM D790 |
| Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 77.0 MPa | ASTM D790 |
| Notched Izod Impact -30 °C 23 °C |
430 J/m 530 J/m |
ASTM D256 |
| Instrumented Dart Impact, Total Energy -30 °C 23 °C |
47.0 J 54.0 J |
ASTM D3763 |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
123 °C 104 °C |
ASTM D648 |
| CLTE, Flow(-40 - 40 °C) | 8.1E-5 cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
| Processing | Nominal Value |
| Drying Temperature<Extrusion Blow Molding> | 100 - 110 °C |
| Drying Time | 3 - 4 hrs |
| Drying Time, Cumulative<Extrusion Blow Molding> | 24 hrs |
| Minimum Moisture Content<Extrusion Blow Molding> | 0.04 % |
| Maximum Moisture Content<Extrusion Blow Molding> | 0.04 - 0.05 % |
| Melt Temperature, Parison | 245 - 260 °C |
| Barrel - Zone 1 Temperature<Extrusion Blow Molding> | 240 - 250 °C |
| Barrel - Zone 2 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
| Barrel - Zone 3 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
| Barrel - Zone 4 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
| Adapter - Zone 5 Temperature<Extrusion Blow Molding> |
245 - 260 °C |
| Head - Zone 6 - Top Temperature<Extrusion Blow Molding> |
245 - 260 °C |
| Head - Zone 7 - Bottom Temperature<Extrusion Blow Molding> |
245 - 260 °C |
| Screw Speed <Extrusion Blow Molding> | 20 - 50 rpm |
| Extruder Feed Zone Temperature<Extrusion Blow Molding> |
60 - 80 °C |
| Mold Temperature<Extrusion Blow Molding> | 40 - 90 °C |
| Die Temperature<Extrusion Blow Molding> | 250 - 265 °C |
25kg/ carton or 25kg/bag, or per your requirement
Hebei Baiyi Import and Export Co., Ltd. is an export-oriented enterprise which also has manufacturing and marketing teams. With a great reputation in China in the chemicals industry and have many years experience in manufacturing and marketing, We will be your most reliable high quality supplier.
Hebei Baiyi Import and Export Co., Ltd. is located in Shijiazhuang, Hebei province and has its own factories, Hebei province. The factories specialize in manufacturing many kinds of chemical products.To ensure the top quality of our products, cutting-edge scientific techniques and advanced management systems are used and strict quality control standards are implemented in every step of manufacturing. In addition, we are representing and acting as the sales agents of other producers in China to make up temporary demand so that we can improve our service to customers globally.
The essence of our business is commitment to customer service by meeting and/or exceeding our client's expectations of cost, quality, and efficient service. We are confident that our competitive edge will provide the foundation required for our customers to be successful in their own market areas.
Our company offers variety of products which can meet your multifarious demands. We adhere to the management principles of "quality first, customer first and credit-based" since the establishment of the company and always do our best to satisfy potential needs of our customers. Our company is sincerely willing to cooperate with enterprises from all over the world in order to realize a win-win situation since the trend of economic globalization has developed with anirresistible force.
){kind=link}